Tantalum FoilShenzhen Sunrise Metal Industry Co.,Ltd

0086-0755-27185042 
http://www.sunriseta.com
sales@sunriseta.comTantalum sheet, Tantalum plate, Ta10w tantalum plate, Spinneret tantalum sheet

Purity　　 : 99.95％min or 99.99％min conformity with ASTM B 708 98
Size:
　　　　　　　　 Thickness (mm)　　　　 Width (mm)　　　　 Length (mm)
Foil　　　　　       0.03-0.07　　　　　　　　30-200　　　　　　　>50
Sheet　　　　      0.07-0.5　　　　　　　　  30- 700　　　　　　  30-2000
Board　　　　      0.5-10　　　　　　　　　  50-1000　　　　　　 50-3000
Purity:　　　       >=99.95％ or 99.99％

Table 1:Chemical composition
Table 2. Mechanical requirements　 (annealed　 condition)

Grade and size	Annealed
	Tensile strength min， psi (MPa)	Yield strength min，psi (MPa)(2％)	Elongation min， ％ (1 inch gage length)
Sheet， foil. and board (RO5200， RO5400)　Thickness<0.060"(1.524mm) Thickness≥0.060"(1.524mm)	30000 (207)	20000 (138)	20
	25000 (172)	15000 (103)	30
Ta-10W　(RO5255) Sheet， foil. and board	70000 (482)	60000 (414)	15
	70000 (482)	55000 (379)	20
Ta-2.5W(RO5252) Thickness<0.125" (3.175mm) Thickness≥0.125" (3.175mm)	40000 (276)	30000 (207)	20
	40000 (276)	22000　(152)	25
Ta-40Nb　　　(RO5240) Thickness<0.060"(1.524mm)	40000 (276)	20000 (138)	25
Thickness>0.060"(1.524mm)	35000 (241)	15000 (103)	25

Properties

Molecular Weight	180.94
Appearance	Solid
Melting Point	2996 °C
Boiling Point	5425 °C
Density	16.654 g/cm3
Thermal Expansion	(25 °C) 6.3 µm·m-1·K-1
Poisson Ratio	0.34
Vickers Hardness	873 MPa
Young's Modulus	186 GPa
Tensile Strength	up to 130,000 psi
Thermal Conductivity	0.575 W/cm/K @ 298.2 K
Electronegativity	1.5 Paulings
Specific Heat	0.0334 Cal/g/K @ 25 °C
Heat of Vaporization	180 K-Cal/gm atom at 5425 °C